Experimental and numerical investigation of fracture toughness and abrasion resistance of thermal spray coated surfaces

Document Type : Original Article

Authors
Mostafa Baran pour 1
Meisam Mohammadi 2
Afshin Iranmanesh 1
1 Department of Mechanical Engineering, Vali-e-Asr University of Rafsanjan, Rafsanjan, Iran.
2 Department of Mechanical Engineering, Vali-e-Asr University of Rafsanjan, Rafsanjan, Iran
10.22067/jacsm.2025.90568.1295
Abstract
Fracture toughness is one of the most important factors in engineering designs. Hence, for designing, repair and maintenance of devices in abrasive, corrosive and oxidative environments, thermal spray method is used for coating the surfaces of devices. For determining the toughness of coated parts, and depending on the loading condition and material properties, different methods are used in industries. In the present study, ASTM standard is applied for determining the test samples conditions and also KIC as the toughness parameter is investigated. Thermal spray test is used for coating the surfaces where the effect of different factors in spraying is considered. Latter, finite element analysis using the relevant software is utilized for simulating and analyzing the fracture toughness of coated samples. Finally, the results of empirical tests and finite element method are compared and the effects of coating methods and coating parameters are investigated in details for the first time.
Keywords
ASTM standard
Thermal spray method
Fracture toughness
Finite element solution
Abrasion
Corrosion
Subjects
[1] “Drilling Industry Magazine,” no 12 and 13, p. 164, 2017.
[2] Saini, H. D. Kumar and V. N. Shukla, “Hot Corrosion behaviour of Nanostructured Cermet based Coatings Deposited by Different Thermal Spray Techniques: A Review,” Materials Today: Proceedings, vol. 4, no. 2, 2017. https://doi.org/10.1016/j.matpr.2017.01.055
[3] J. A. Joyce , D. Wells, B. Stoltz, L. Shelton, P. Jacobs and R. E. Link, “Evaluating the Fracture Toughness of Layered Pressure Vessel Steels,” Engineering Fracture Mechanics, vol. 207, 2018. https://doi.org/10.1016/j.engfracmech.2018.11.039
[4] F. Fanicchia, X. Maeder, J. Ast, A. A. Taylor, Y. Guo, M. N. Polyakov, J. Michler and D. A. Axinte “Residual stress and adhesion of thermal spray coatings: Microscopic view by solidification and crystallisation analysis in the epitaxial CoNiCrAlY single splat,” Materials & Design, vol. 153, 2018. https://doi.org/10.1016/j.matdes.2018.04.040
[5] P. Lin, J. Guan, H. Peng and J. Shi, “Horizontal cracking and crack repair analysis of a super high arch dam based on fracture toughness,” Engineering Failure Analysis, vol. 97, 2019. https://doi.org/10.1016/j.engfailanal.2019.01.036
[6] H. F. Li, Q. Q. Duan, P. Zhang, X. H. Zhou, B. Wang and Z. F. Zhang “The quantitative relationship between fracture toughness and impact toughness in high-strength steels,” Engineering Fracture Mechanics, vol. 211, 2019. https://doi.org/10.1016/j.engfracmech.2019.03.003
[7] E. PourSaidi and M. KhoshNejhad, “Investigation and determination of changes in mechanical properties of plasma spray heat-resistant coatings under thermal loading using the indentation test method,” Master Thesis, Zanjan Univesrity, Iran, 2017.
[8] M. E. Alami, S. Feli and Gh. Sarifi, “ Modeling the impact of molten particles on the substrate,” Master Thesis, Razi Univesrity, Iran, 2012.
[9] S. Mansouri, S. Mirzaei, M. Shariati and N. Ziari, “Evaluation of the accuracy of different methods for measuring rock fracture toughness in tension and shear conditions using laboratory studies and numerical modeling,” Master Thesis, Shahrood Univesrity, Iran, 2013.
[10] S. H. Hashemi, M. KimiaBakhsh and M. Rezai Yekta, “Experimental and numerical determination of fracture toughness using Charpy impact test data in API X65 grade gas transmission pipe steel,” ISME 2011. https://doi.org/10.22060/mej.2013.316
[11] F. Ashna Ghasemi, F. Ali Gholi Zade and A. Poor Kamali, “Experimental Investigation of the Effect of Temperature on the Low Velocity Impact Response of Grooved Aluminum Plates Repaired by Metal Laminated Composite Adhesives (FML),” Modares Mechanical Engineering Journal, vol. 14, no. 9, 2014.
[12] R. Ahadi, H. Harati Zadeh and M. Mohammadi, “Investigation of mechanical properties and abrasion resistance of titanium-based ceramic nanocoatings,” Master Thesis, Shahrood Univesrity, Iran, 2019.
[13] S. Matthews, and L.M. Berger, “Inter-diffusion between thermally sprayed Cr3C2-NiCr coatings and an Alloy 625 substrate during long-term exposure at 500 °C, 700 °C and 900 °C,” Journal of Alloys and Compounds, vol 770. 2019. https://doi.org/10.1016/j.jallcom.2018.08.189
[14] S. Nouroozi, R. Moharrami, H.R. Salimi and M. Jalali, “Evaluation of the effect of effective parameters of HVOF thermal spraying process on residual stress and bond strength of WC-12Co coating ,” Master Thesis, Nooshirvani Babol Univesrity, Iran, 2013.
 
Send comment about this article
Enter Name.
Enter a valid email address.
Enter a vaid affiliation.
Enter comments (At leaset 10 words)
CAPTCHA Image
Enter Security Code Correctly.